Andialusit g'ishtni qanday qilish kerak?
Andalusit bilan umumiy, baland alumina baoksitli klinker, Sillimanit va loyni matritsa kabianalimus g'ishtlariTorpedo temir tanklari uchun ishlab chiqarilishi mumkin.
Ishlab chiqarish bosqichlari:
Andalusi - ishlatilgan va ishlatilgan. Yuqori alumina boksit klinker va loydan foydalanish uchun tebranadigan ball tegirmonida aralash va zamin. Xom ashyo nisbati quyidagicha: analusit {{1} {{2} {{4} {{4}% va lira {{5}%. Aralashtirish uchun g'ildirak tegirmonidan foydalaning. Aralashganda, katta zarralar va o'rta zarralarni qo'shing, 2-3 daqiqa uchun quruq aralash, so'ngra bog'lang va birga silliqlang. Jami aralash vaqt 15 daqiqa. Mudning zarrachalari tarkibi: {8}} {{1 {{{{0} 1-0} 1-0} 5-0. 088 mm 10.5%,<0.088mm 43%. After 25 hours of trapping, the clay is formed by a 630t friction brick press, with a density of 2.65-2.75g/cm³. After drying, the product is fired in a tunnel kiln, with a maximum firing temperature of 1350℃ and a heat preservation of 8 hours.
Jismoniy ko'rsatkichlar:
Mahsulotning asosiy jismoniy ko'rsatkichlari: 2,48g / sm³, xona harorati (1450 daraja, 2h) (1400 dona, 2h) (1100 dona suvni sovutish) (1100 dona suvni sovutish).